History & Manufacture of Portland Cement Concrete Basics Home > History & Manufacture of Portland Cement


In 1824, Joseph Aspdin, a British stone mason, obtained a patent for a cement he produced in his kitchen. The inventor heated a mixture of finely ground limestone and clay in his kitchen stove and ground the mixture into a powder create a hydraulic cement-one that hardens with the addition of water. Aspdin named the product portland cement because it resembled a stone quarried on the Isle of Portland off the British Coast. With this invention, Aspdin laid the foundation for today's portland cement industry.

Types of Portland Cement
Different types of portland cement are manufactured to meet various physical and chemical requirements. The American Society for Testing and Materials (ASTM) Specification C-150 provides for eight types of portland cement.Type I portland cement is a normal, general-purpose cement suitable for all uses. It is used in general construction projects such as buildings, bridges, floors, pavements, and other precast concrete products. Type IA portland cement is similar to Type I with the addition of air-entraining properties. Type II portland cement generates less heat at a slower rate and has a moderate resistance to sulfate attack. Type IIA portland cement is identical to Type II and produces air-entrained concrete. Type III portland cement is a high-early-strength cement and causes concrete to set and gain strength rapidly. Type III is chemically and physically similar to Type I, except that its particles have been ground finer. Type IIIA is an air-entraining, high-early-strength cement. Type IV portland cement has a low heat of hydration and develops strength at a slower rate than other cement types, making it ideal for use in dams and other massive concrete structures where there is little chance for heat to escape. Type V portland cement is used only in concrete structures that will be exposed to severe sulfate action, principally where concrete is exposed to soil and groundwater with a high sulfate content.

 Portland cements can also be made to ASTM C1157 and include the following: Type GU hydraulic cement for general construction, Type HE-high-early-strength cement, Type MS-moderate sulfate resistant cement, Type HS-high sulfate resistant cement, Type MH-moderate heat of hydration cement, and Type LH-low heat of hydration cement. These cements can also be designated for low reactivity (option R) with alkali-reactive aggregates.